@Article{JFBI-16-1,
author = {Yao, Si-Rui and Meng, Chen and Qing-Hong, Huang and Ze-Kun, Liu and Yi, Li, Henry},
title = {Effects of Dip-Coating Processing Parameters on the Functional Performances of Ti$_3$C$_2$T$_x$ MXene-Silk Yarns},
journal = {Journal of Fiber Bioengineering and Informatics},
year = {2023},
volume = {16},
number = {1},
pages = {15--30},
abstract = {<p style="text-align: justify;">Mxenes, as a new group of two-dimensional materials in form of transition metal carbides, carbonitrides
and/or nitrides, have been playing an important role in the wearable smart electronic field. Due to their
abundance surface functional groups, Mxenes have showed their superior dispersions in various solvents
which is beneficial to simply the fabrication process of textile-based electronics while their electrical
performance guaranteed. In this work, we report a novel fine silk yarn dip-coated in an aqueous solution of ${\rm Ti}_3{\rm C}_2{\rm T}_x$ MXene to obtain low electrical resistance (∼25.6 Ohms/cm). Yarns structures and morphologies
were observed by transmission and scanning electron microscopy (TEM &amp; SEM) together with energy
dispersive spectroscopy (EDS). Besides, Fourier transform infrared (FTIR) and Raman spectroscopy, and
X-ray diffraction (XRD) analysis were carried out to reveal the chemical compositions. By controlling
two coating parameters as design of experiments (DoE) factors, we found both solution concentration
and soaking time had significant effects on yarn performances. The mechanical performance of yarn
fabricated under the optimised coating condition was evaluated by means of tensile testing, resulting in
a significant 23% increase in breaking strength (∼107 MPa). In responding to tensile deformation, the
dip-coated yarn also performed a linear variation in resistance, which indicated its capability in sensing
applications.</p>},
issn = {2617-8699},
doi = {https://doi.org/10.3993/jfbim01041},
url = {https://global-sci.com/article/86348/effects-of-dip-coating-processing-parameters-on-the-functional-performances-of-ti-3c-2t-x-mxene-silk-yarns}
}