abstract = {<p>Wet electrospinning is a convenient and versatile method to produce nanofibers. When adding an active
agent into the bath solution, functional fibers may be fabricated in the fiber-forming process. In this
paper, the spinnability of PA6/CS-NPs hybrid nanofiber filaments was studied which might obtain
antibacterial activity. Three dispersants were selected, including span-80 and tween-80 (ST) (1/1, w/w),
sodium polyacrylate (PAAS) and methyl cellulose (MC) to improve the dispersibility of the chitosan
nanoparticles (CS-NPs) in the Peregal O aqueous solution. The mixture of ST was finally determined to
be applied in the bath solution mainly because the agglomeration of CS-NPs could be largely reduced
and the suspension of CS-NPs be maintained comparatively stable, and the continuous spinning time was
longer than the others. When ST was added into the bath solution to fabricate the fibers, by varying the
compositions of the bath solution, including concentrations of the CS-NPs and ST, the morphologies of
PA6/CS-NPs fibers were investigated. When the composition of the bath solution was 0.2 wt.% ST and
0.4 wt.% CS-NPs, the maximum number of CS-NPs could be observed on the surface of the nanofibers.
Compared to the pure PA6 nanofiber filaments, the mechanical properties of the PA6/CS-NPs hybrid
nanofiber filaments would be weakened.</p>},