title = {Preparation and Characterization of the Electro-Spun Polyethylene Terephthalate Fibrous Membrane},
journal = {Journal of Fiber Bioengineering and Informatics},
year = {2014},
volume = {7},
number = {2},
pages = {199--208},
abstract = {In this study, the electro-spun PET (polyethylene terephthalate) fibrous mats with fiber diameters
ranging from 400 nm to 6 μ m were produced with the different settings of the polymer solution
concentration, spinning voltage and receiving distance. The morphological properties and structure of the
fibrous membrane were evaluated for the investigation of the effects of the electro-spinning parameters on
fiber properties using Scanning Electron Microscopy (SEM) and X-ray Diffraction (XRD) respectively.
The experimental results showed that the continuous PET fibers without beads can be spun with the
following settings: spinning voltage at 20 kv, receiving distance at 15 cm, and concentration of polymer
solution 10%-16%. The electro-spinning process can be controlled well at a spinning voltage of 16-22 kv.
The effects of receiving distance on the fiber diameter and morphological structure were not obvious;
however, the crystallinity of the PET fibers was relatively lower than other spinning methods.},