A series of composites of carbon fibre-reinforced polyamide1012 (PA1012) were prepared which the carbon fibre content was from 5% to 40%. Their thermo-mechanical properties and fracture morphology were characterized by means of thermogravimetric analysis (TGA), a microcomputer-controlled electronic universal tester, and Scanning Electron Microscopy (SEM), respectively. The results showed that the initial decomposition temperature of the composite was above 400C. With the increase in carbon fibre content, the tensile strength and elastic modulus of the composites were improved. When the carbon fibre content was 15%, it was found that the maximum values of tensile strength and elastic modulus were 87.01 MPa and 438.31 MPa, respectively. The images of SEM showed that the surface modified carbon fibre was superior to original carbon fibre. It was also observed that the surface of modified carbon fibre had some particles that may have contained the ester group, which could have improved the interfacial bonding strength.
You do not have full access to this article.
Already a Subscriber? Sign in as an individual or via your institution
Journal Article Details
Publisher Name: Global Science Press
Language: English
DOI: https://doi.org/10.3993/jfbim00279
Journal of Fiber Bioengineering and Informatics, Vol. 11 (2018), Iss. 1 : pp. 41–47
Published online: 2018-01
AMS Subject Headings:
Copyright: COPYRIGHT: © Global Science Press
Pages: 7
Keywords: Carbon Fibre
Author Details
-
Novel Composites of Poly(vinyl chloride) with Carbon Fibre/Carbon Nanotube Hybrid Filler
Skórczewska, Katarzyna | Lewandowski, Krzysztof | Wilczewski, SławomirMaterials, Vol. 15 (2022), Iss. 16 P.5625
https://doi.org/10.3390/ma15165625 [Citations: 8] -
Mechanical and Dynamic Properties of Biocomposites
Dynamic Properties of Kenaf‐Fiber‐Reinforced Composites
Al Mizan, Rashed | Akter, Nur N. | Iqbal, Mohammad I.2021
https://doi.org/10.1002/9783527822331.ch9 [Citations: 0]