One kind of composite membrane by combining electrospun nanofibrous membrane with fiberglass mesh was developed for air filtration. The fiber diameter, morphology of membranes, pressure drop and filtration efficiency of composite membrane were evaluated. The results revealed that the pressure drop and filtration efficiency of composite membrane decreased with the increase of winding speed (the higher winding speed is, the less of nanofibers are). The pressure drop of all samples at an airflow speed of 5 m/min was less than 25 Pa, which was much lower than the values from other reported work; and the highest filtration efficiency of sample in this work was more than 83% for particulate matters with 1.88 m.
You do not have full access to this article.
Already a Subscriber? Sign in as an individual or via your institution
Journal Article Details
Publisher Name: Global Science Press
Language: English
DOI: https://doi.org/10.3993/jfbim00272
Journal of Fiber Bioengineering and Informatics, Vol. 10 (2017), Iss. 4 : pp. 223–230
Published online: 2017-01
AMS Subject Headings:
Copyright: COPYRIGHT: © Global Science Press
Pages: 8
Keywords: Electrospinning
-
Mikrofiltrasyon için elektrolif çekim yöntemi ile üretilmiş PVDF nanolifli membranlar: Gözenek boyutu ve kalınlığının membran performansına etkisi
Akduman, Çiğdem
European Journal of Science and Technology, Vol. (2019), Iss. P.247
https://doi.org/10.31590/ejosat.556748 [Citations: 4] -
Cellulose acetate and polyvinylidene fluoride nanofiber mats for N95 respirators
Akduman, C
Journal of Industrial Textiles, Vol. 50 (2021), Iss. 8 P.1239
https://doi.org/10.1177/1528083719858760 [Citations: 43]